Puncture resistance denotes the relative ability of a material to inhibit the progression of a tear once it has been pierced by a cut or a nick. Tests devised to measure puncture resistance are generally application-specific, covering items such as roofing〔(Test Method for Static Puncture Resistance of Roofing Membrane Specimens )〕 and packaging materials, protective gloves, needle disposal facilities,〔(Standard Specification for Puncture Resistance of Materials Used in Containers for Discarded Medical Needles and Other Sharps )〕 bulletproof vests, tires, etc. Puncture resistance in fabrics can be obtained through very tight woven fabrics, small ceramic plates in fabric coating or tight woven fabrics with a coating of hard crystals. All described methods significantly reduce the softness and flexibility of the fabric. The puncture resistance will depend on the nature of puncture attempt, with the two most important features being point sharpness and force. A fine sharp point such as a hypodermic needle will require a high ability to absorb and distribute the force to avoid penetration, but the total forces applied are still limited. The EN388 glove standard use a more pencil-like object with a flat tip of 1mm diameter. The EN388 test is highly dependent on the materials ability to withstand high forces through high tenacity and to a lesser extent to avoid cut or separation of the material. There is no or limited correlation between the protections provided in the low force/needle protection and the high force/pencil like EN388 test. Needle-resistant materials as described above are generally pierced by a force between 2-10N by a 25 gauge needle perpendicular to the fabric. The forces in the EN 388 test results are rated according to a score from 0-4 (0-<20N, 1-20N, 2-60N 3-100N 4-150N+). ==See also== *Fracture toughness *ASTM International *Aramid 抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』 ■ウィキペディアで「Puncture resistance」の詳細全文を読む スポンサード リンク
|